Super Glue EPOXY 90s Instant Set 28.3g (1oz) in dispenser

Superfast 90s 2-component epoxy adhesive, high strength 10min. Packing double dose dispenser (syringe) 28 g (1/2 P + T).

5MB80SY-IN48

New product

ZAP

In stock: > 10 pcs
Stores and delivery dates
Price with VAT::
4,25 € 4,06 €
Price without VAT:
3,35 €

-0,19 €

B B

More info

More info

Extremely fast curing, two-component epoxy adhesive with high strength, resistant to fuel and vibration; after complete curing, easily grindable. He does not bark aging.

Properties

  • The mixing ratio of the components: 1: 1 (by volume and by weight)
  • Initial color: clear to amber
  • Final color: slightly yellow
  • Working Time (to Gel): 90 seconds (18 ° C to 27 ° C)
  • The glued parts can be manipulated: after 10 minutes
  • Full cure: 24 h
  • Gap filling capability: max. 6 mm
  • Hardness (Shore, D): 75-85 (after full cure)
  • Shear Strength (on steel): 13,790 kPa (± 20%)
  • Temperature resistance of bonded joint: -40 ° C to + 60 ° C

Removing excess uncured adhesive: a cloth or paper napkin moistened with denatured alcohol.

Dilution: thinner for S6300 epoxy varnish (use of thinner extends the cure time and reduces final bond strength - if you need a "thinner" epoxy, use a low viscosity laminating or finishing epoxy).

Use as sealant, suitable fillers: microballoons, talc, baby powder, kieselguhr, fine balsamic or lime sawdust, chopped glass fibers. Attention - addition of the filler can reduce the working time by up to 25% and (depending on the type and amount of filler used) may reduce the strength of the joint.

Suitable for bonding: soft and hard wood, chipboard, plywood, metals, foamed polystyrene, ceramics, porcelain, glass and carbon laminates, glass and carbon fabrics and fibers.

Not suitable for bonding: soft and flexible plastics (including EPP and EPO), polyethylene, teflon.

Storage: in a tightly closed package, in cold, dry and dark. Do not expose to temperatures below 5 ° C. Be careful to keep the cap clean and to put it properly - even a small amount of hardener can degrade a large amount of resin. < / p>

Shelf life: When the correct storage conditions are met, the manufacturer guarantees a shelf life of 1 year, while maintaining the above mentioned product properties. Practical experience shows that Super Glue epoxies retain their excellent properties for many years (see also Note 2) for proper storage, due to the low volume of adhesive glue you do not have to worry about its life at all.

Note: 1: Curing of the adhesive depends mainly on the ambient temperature; if you mix a larger amount of epoxide at a time (typically more than 20-30 g), it can be harder to cure - in order to maintain longer working hours, the adhesive should be cooled, for example, in a water bath. This is due to the heat release of the resin and hardener and, at a higher temperature, the resin cure faster. And, as the volume increases, the weight of the resin (and hence the amount of heat generated) increases faster than the surface of the outer surface from which the heat is drawn to the surrounding area, the larger the amount of resin is heated and cured faster. Do not you believe? Believe! The 1 cm cube has a volume of 1 cm3 and a surface of 6 cm2 - a ratio of 6: 1 while a 2 cm side cube has a volume of 8 cm3 and a surface of 24 cm2 - a ratio of only 3: 1!

Note: 2: Originally clear and quite well liquid epoxy resins can sometimes thicken ("scratch" like bee honey) and lose transparency - due to exposure to low temperatures, humidity or time. Carefully warm it up in hot water (60-70 ° C) for a few minutes until the resin becomes clean again in the whole volume, again giving you the "new" resin with its original properties. This is the official recommendation of the manufacturer. A quick but slightly risky alternative is to heat the resin in the microwave for 10-15 seconds at 750 W - no more! Attention, the resin container must be open to prevent it from splashing when it is too hot. < / i>

The product contains substances classified as dangerous according to Regulation (EC) No 1272/2008. See the "Download" section for details.